Pengaruh pH dan Tegangan Listrik dalam Elektrolisis Limbah Padat Baja (Slag Eaf) Sebagai Upaya Mereduksi Kandungan Logam Fe pada Limbah Padat Industri Galvanis

Abdul Aziz; Wirda Udaibah; Malikhatul Hidayah

doi:10.21580/wjc.v2i2.3102

Pengaruh pH dan Tegangan Listrik dalam Elektrolisis Limbah Padat Baja (Slag Eaf) Sebagai Upaya Mereduksi Kandungan Logam Fe pada Limbah Padat Industri Galvanis

* - Program Sarjana Jurusan Kimia Fakultas Sains dan Teknologi UIN Walisongo, Indonesia

- Jurusan Kimia Fakultas Sains dan Teknologi UIN Walisongo, Indonesia

(*) Corresponding Author

DOI: 10.21580/wjc.v2i2.3102

Abstract
References
Licensing
How to cite

Galvanization is a metal coating process that is widely used in industry. The effects of this metal coating process are not entirely beneficial to society. The issue of pollution generated by the metal coating activity becomes very important. The objective of this research is to reduce Fe metal content from solid waste steel using electrolysis process with variation of pH of electrolyte solution and voltage. This research uses experimental method with test of metal content composition using X-Ray Flouresence, and Fe metal reduction using electrolysis process. This research activity used stainless steel plate as cathode and solid steel waste chunk as anode. Variations of pH of FeSO₄.7H₂O electrolyte solution used during electrolysis process are pH = 2, pH = 2.5, pH = 3, pH = 3.5 and pH = 4. Variation of electric voltage used is 3 volts, 6 volts, 9 volts and 12 volts. The result of purity level analysis of the initial Fe metal at anode was 84,48 %, while after electrolysis process there was an increase of metal purity attached to the cathode of 96,58 %. The result showed that the effect of pH variation of the electrolyte solution on the mass produced in the electrolysis process in the A₁, A₂, A₃, A₄ and A₅ samples was 0,09; 0,07; 0,02; 0,02; and 0,02 g. The greater the concentration of H⁺ of the electrolyte solution the more mass produced. In variable voltage of electricity on samples A₁₁, A₂₁, and A₃₁ mass produced that is equal to 0,14; 0,13; and 0,10 g. While the mass of A₄₁ sample did not increase in the cathode produced during the electrolysis process. The greater the voltage used in the electrolysis process the greater the mass produced.

Keywords: Fe metal; solid waste steel; electrolysis

Chang, Raymond. 2005. Kimia Dasar Jilid 2. Jakarta: Erlangga.
Chen, Xueming, dkk. 2002. Investigation On The Electrolysis Voltage of Electrocoagulation. Chemical Engineering Science.
Farid, Ahmad dan Nur Wahid. 2009. Proses Elektrolisis untuk Pengambilan Seng dari Limbah Padat Industri Galvanis. Semarang: UNDIP.
Gunawan, G., dkk. 2011. Pemanfaatan Slag Baja untuk Teknologi Jalan Yang Ramah Lingkungan. Bandung: Kementerian Pekerjaan Umum.
Izaki, Masanobu. 2010. Modern Elektroplating Fifth Edition.
Manurung, Charles. (n.d.). Pengaruh Kuat Arus Terhadap Ketebalan Lapisan dan Laju Korosi (MPY) Hasil Elektroplating Baja Karbon Rendah dengan Pelapis Nikel. Medan.
Palar, Heryando. (2008). Pencemaran dan Toksikologi Logam Berat. Jakarta: Rineka Cipta.
Slamet, Juli Soemirat. (2009). Kesehatan Lingkungan, Yogyakarta: Gadjah Mada University Press.